316 / 316L rostfri stålspole
Specifikationer | ASTM A240, ASME SA240 |
Standard | JIS, ASTM, AISI, GB, EN, DIN |
Yta | 2B, BA, HL, nr 4, spegel etc. |
Avsluta | Kallvalsad, varmvalsad |
Tjocklek | 0,3 mm – 100 mm |
Storlek | 1000mm, 1219mm, 1250mm, 1500mm, 1524mm, 2000mm |
Betygsspecifikationer för rostfritt stål 316 / 316L-spolar
STANDARD | WERKSTOF nr | UNS | JIS | BS | GOST | AFNOR | SV |
SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | - | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
Kemiska egenskaper hos SS 316 / 316L-spolar
Kvalitet | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
SS 316 | 0,08 max | 2,0 max | 1,0 max | 0,045 max | 0,030 max | 16.00 - 18.00 | 2.00 - 3.00 | 11.00 - 14.00 | 67,845 min |
SS 316L | 0,035 max | 2,0 max | 1,0 max | 0,045 max | 0,030 max | 16.00 - 18.00 | 2.00 - 3.00 | 10.00 - 14.00 | 68,89 min |
Mekaniska egenskaper hos SS 316 / 316L-spolar
Densitet | Smältpunkt | Brottgräns | Avkastningsstyrka (0,2% offset) | Förlängning |
8,0 g / cm3 | 1400 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |
8,0 g / cm3 | 1399 ° C (2550 ° F) | Psi - 75000, MPa - 515 | Psi - 30000, MPa - 205 | 35 % |