304L rör i rostfritt stål ASME SA213 TP304L ASTM A213 TP304L
ASTM A269 304L rostfritt stålrör, ASTM A213 SA213 TP304L rostfritt stålrör, ASTM A312 SA312 TP 316L rostfritt stålrör, rostfritt stål 304L rör, ASTM A213 SA213 304L U-böjrör, EN 10216-5 1.4307 Rostfritt stålrör i Kina. ASTM A312 SA312 TP 316L Rostfritt stålrör, Rostfritt stål 304L rör, ASTM A213 SA213 304L U-rör, EN 10216-5 1.4307 Rostfria stålrör i Kina. Rostfritt stål 304L rör.
Utvändig diameter: 6-530 mm
Väggtjocklek: 0,50 - 64 mm
Standard specifikation:
EN 10216-5; DIN 17456, DIN 17458, DIN 2462, DIN 17455
GB / T14975; T14976; T13296; GB5310;
ASTM A213, A269, A312, A511, A789, A790, A928, A999, A1016, ASTM B161, ASTM B163, ASTM B165, ASTM B167, ASTM B338, ASTM B407, ASTM B423, ASTM B444, ASTM B43 B626, ASTM B668, ASTM B677, ASTM B829
JIS G3459, JIS G3463, JIS G3446, JIS G3447, JIS G3448, JIS G3468
GOST 9940; GOST 9941;
Kemisk sammansättning:
| Kvalitet | - | C | Mn | Si | P | S | Cr | Mo | Ni | N |
| 304L / S30403 | min Max. | -0.035 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | - | 8.0-12.0 | - |
| 304 / S30400 | min Max. | -0.08 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | - | 8.0-11.0 | - |
| EN 10216-5 1.4301 | min Max. | -0.07 | -2 | -1 | -0.04 | -0.015 | 17.00-19.5 | - | 8.0-10.5 | -0.11 |
| EN 10216-5 1.4307 | min Max. | -0.03 | -2 | -1 | -0.04 | -0.015 | 17.5-19.5 | - | 8.0-10.0 | -0.11 |
| 304H / S30409 | min Max. | 0.04-0.10 | -2 | -1 | -0.045 | -0.03 | 18.0-20.0 | - | 8.0-11.0 | - |
| EN 10216-5 1.4948 | min Max. | 0.04-0.08 | -2 | -1 | -0.035 | -0.015 | 17.0-19.0 | - | 8.0-11.0 | -0.11 |
Mekaniska egenskaper:
| - | Brottgräns | Sträckgräns | Förlängning | Hårdhet | Hårdhet |
| Kvalitet | (MPa) min | 0,2% bevis (MPa) min | (% i 50 mm) min | Rockwell B (HR B) max | Brinell (HB) max |
| 304L | 485 | 170 | 35 | 90 | 192 |
| 304 | 515 | 205 | 35 | 90 | 192 |
| 304H | 515 | 205 | 35 | 90 | 192 |
Fysikaliska egenskaper:
| 304L rörtäthet i rostfritt stål (lb / cu. In.) | 0.29 |
| Specifik vikt (g / cm³) | 7.93 |
| Specifik värme (Btu / lb / Deg ° F - [32-212 Deg ° F]) | 0.12 |
| Elektrisk motståndskraft (mikrohm-cm (vid 68 ° F)) | 432 |
| Smältpunkt (Deg ° F) | 2650 |
| Modulus of Elasticity Tension | 28 |